Physical | Test Method | Unit | Value LW/CW | |
E23 | E17 | |||
Tensile Strength | ASTM D-638 | MPa | 300/55 | 200/45 |
Tensile Modulus | ASTM D-638 | GPa | 23/7 | 17/5 |
Compressive Strength | ASTM D-695 | MPa | 250/70 | 200/70 |
Compressive Modulus | ASTM D-695 | GPa | 20/7 | 15/5 |
Flexural Strength | ASTM D-790 | MPa | 300/100 | 200/70 |
Full Section | EN13706-2 | GPa | 23 | 17 |
Interlaminar Shear Strength | ASTM D-2344 | MPa | 25 | 20 |
Density | ASTM D-792 | g/cm3 | 1.72—1.94 | |
Barcol Hardness | ASTM D-495 | >45 | ||
Water Absorption | ASTM D-570 | % max | 1 | |
Physical | Test Method | Unit | Value LW/CW | |
E23 | E17 | |||
Tensile Strength | ASTM D-638 | MPa | 300/55 | 200/45 |
Tensile Modulus | ASTM D-638 | GPa | 23/7 | 17/5 |
Compressive Strength | ASTM D-695 | MPa | 250/70 | 200/70 |
Compressive Modulus | ASTM D-695 | GPa | 20/7 | 15/5 |
Flexural Strength | ASTM D-790 | MPa | 300/100 | 200/70 |
Full Section | EN13706-2 | GPa | 23 | 17 |
Interlaminar Shear Strength | ASTM D-2344 | MPa | 25 | 20 |
Density | ASTM D-792 | g/cm3 | 1.72—1.94 | |
Barcol Hardness | ASTM D-495 | >45 | ||
Water Absorption | ASTM D-570 | % max | 1 | |